Aluminium Foil Adhesive is a water-based laminating adhesive polymerized from special monomers for bonding aluminum foil to a variety of paper grades. It is supplied as a milky liquid with 54 ± 0.5% solid content and a low viscosity of 50-110 mPa·s, which lets it wet out the foil surface and flow evenly through the coating station at production speed. Good fluidity makes the product easy to operate.
The adhesive delivers strong initial tack, strong holding power and a high final bond, with an initial adhesive strength of steel ball No. 18 or higher, a holding time above 24 hours and a 180° peel strength of at least 10 N/25 μm. Its superior low-temperature resistance keeps the foil-to-paper bond intact when the laminate is stored or used in cold conditions. The pH is 6.5-8.
Non-toxic, harmless, non-flammable and non-explosive, the product has no adverse effect on operators or the environment and runs on standard laminating lines. It is packed in 200 L drums and 1000 L containers for industrial use. ChemPortal supplies this foil laminating adhesive in wholesale quantities to converters producing foil-paper laminates.
Key features
- Water-based emulsion, 54 ± 0.5% solids, low viscosity of 50-110 mPa·s
- Strong adhesive, initial and holding strength on foil-to-paper laminates
- Initial tack ≥ steel ball No. 18; holding time ≥ 24 hours
- 180° peel strength of at least 10 N/25 μm
- Superior low-temperature resistance for cold-stored laminates
- Non-toxic, non-flammable and non-explosive; supplied in 200 L and 1000 L
Applications
- Lamination of aluminum foil with various papers
- Foil-backed paper composites
- Laminates exposed to low-temperature storage or use
- Water-based foil converting lines
- Paper-foil composites requiring high peel strength
Technical parameters
| Parameter | Value |
|---|---|
| Appearance | Milky liquid |
| Viscosity | 50-110 mPa·s |
| Solid content | 54 ± 0.5% |
| pH | 6.5-8 |
| Initial adhesive strength | ≥18# Steel Ball |
| Holding adhesive time | ≥24h |
| 180° Bonding strength | ≥10N/25μm |
On a small screen, scroll the technical table horizontally.
Packaging & logistics
Standard packaging options. Confirm the packaging, lot size and delivery terms with your quotation.
Frequently asked questions
What does this aluminum foil adhesive bond?
It is formulated for laminating aluminum foil to various kinds of paper. The low viscosity and good fluidity let it coat evenly and wet the foil surface, while strong initial and holding strength give a durable composite. A 180° peel strength of at least 10 N/25 μm is typical.
What are the solid content and viscosity, and why is the viscosity so low?
The emulsion has 54 ± 0.5% solid content with a viscosity of only 50-110 mPa·s and a pH of 6.5-8. The low viscosity suits thin, uniform coat weights on foil laminating lines and easy operation; tack is steel ball No. 18 or higher and holding time exceeds 24 hours.
How is the adhesive packaged for wholesale delivery?
It is supplied in 200 L drums and 1000 L containers, which suit continuous laminating operations. As a water-based, non-flammable and non-explosive product it is simpler to transport and store than solvent adhesives; storage conditions and shelf life are given in the technical data sheet.
Does it perform at low temperatures, and how do I get a quote?
Yes, superior low-temperature resistance is one of its main characteristics, so foil-paper laminates keep their bond in cold storage and use. For wholesale pricing, lead time and the technical data sheet, contact ChemPortal with your monthly volume, paper grades and delivery destination.
Published reference specifications. Confirm the current grade, SDS / TDS / COA, packaging and delivery terms with your quotation.